Стекловолоконная смола для Пултрузионных изделий

P411 vinyl resin is typical  kind Epoxy vinyl ester, dissolved into styrol, with good corrosion resistance, chemical mediator resistance and mechanical property, ideal for hand lay , twine and other process FRP products.

liquid resin property

Unit testing method

Appearance transparent light yellow liquid

Acid value 12-20        mgKOH/g   GB/T 2895-2008

Solid content 52-58    %   GB/T 7193-2008

Viscosity 25℃ 0.30-0.50 Pa.s   GB/T 7193-2008

Stability 80℃ ≥24 h   GB/T 7193-2008

Typical curing performance

25℃ water bath,100g resin filled into 2ml methyl ethyl ketone peroxidesolution 4mlcobalt iso-octoate 

Gel time 11.2-20.8    min  accord to GB/T 7193-2008

Rein casting boy typical property(typical data)

unit               testing method

appearance                casting body no fault

Tensile strength      75                  Mpa                 GB/T  2567-2008     

tensile modules of elasticity 3200                Mpa                 GB/T  2567-2008     

Elogation at break    3.00                %                   GB/T  2567-2008     

Bending strength      115              Mpa                 GB/T  2567-2008     

Flexural modulus   3700                Mpa                 GB/T  2567-2008     

Impact strength       18.00                             KJ/m²                              GB/T  2567-2008     

Distortion temperature  105                 ℃                  GB/T  1634-2004      

Barcol hardness      45                                      GB/T  3854-2005      

              Liquid resin package and storage conditions

ü Packed in metal barrel , 220kg/barrel (about 85.6 us gallons)

ü Try to prevent liquid resin from directly sunshine and heat resource

ü Flammable, should keep away from open fire

ü Shelf life is 3 month under 25℃

ü Store and operate in a dry, well-ventilated place

ü Please read MSDS carefully before use this product

Note: This data is determined according to the national standard (GB). Due to many factors in the processing, it is not necessary to exclude the user's own experimental research. It is legally not guaranteed that certain properties of the product are fully applicable to a specific application. And retain the right to modify the information.