Высокопрочный силиконовый каучук rtv2 для изготовления фигурок из

2.Characteristics of high strength rtv2 silicone rubber for fiberglass sculpture figurine brush mold making

*An exceptional fluidity and good operability, easy to demold
*Good tensile strength and tear strength
*Soft hardness
*Copy detailed pattern 
*Good flexibility

*Eco-friendly

*Long shelf-time &lifetime

3.Application of high strength rtv2 silicone rubber for fiberglass sculpture figurine brush mold making

C-815 silicone rubber  is suitable to make mold for concrete stone, cement  casting , gypsum decocations, plaster product, resin craft, soap,candle, bronze casting, wax, crystal, tyre  mold ,shoe mold ,clay casting ,soap mold,ceramic casting ,etc..

4.Datesheet of high strength rtv2 silicone rubber for fiberglass sculpture figurine brush mold making

5. Using instructions of high strength rtv2 silicone rubber for fiberglass sculpture figurine brush mold making

Step 1: Prepare and clean the prototype.q

You must make sure your original molds perfect. fix the original mold on a board , then using some  assistant material(like cardpaper) to make a frame for to surround the prototype. The frame is no need ,if we make the mold  by brushing way

Step 2: Take the silicone and catalyst as the ratio 100:2 (silicone:catalyst=100:2) ,mix the silicone  rubber and   catalyst evenly. 
*Notes: Molding silicon rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of  flowing liquid and  Part B is the curing agent. Remember to mix part A and part B evenly, otherwise the  silicon rubber will be partly solidified and this will bring troubles for your final operation. What’s more, the finished molds will have a short life. All of these  will cause a waste of silicon rubber.

Step 3: Vacuum pumping

After mixed the silicone evenly, it is better to release the bubble by Vacuum pumping.

Step 4: Pouring cast or brushing cast

After released the bubble, we can pour/brush the silicone rubber on the prototype 
*Notes:Please finished all the steped within the operation time .If not it will cause cross linking reaction,  and no more  further steps will be available.So,we have to pay attention to the pot life and curing time.