Product Description

Properties	ISO Test Method	Test Condition	Unit	CM-205
Melt Flow Index	1133	230℃×3.8KG	ml/10 min	1.9
Mass Density	1183	23 ℃	g/cm3	1.19
Tensile Strength	527	5 mm/min, yield	MPa	70
Tensile Strength	527	5 mm/min, break	MPa	70
Tensile Elongation	527	50 mm/min	%	12
Flexural Strength	178	2 mm/min	MPa	103
Flexural Modulus	178	2 mm/min	GPa	2.8
Izod Impact Strength	180/1A	23 ℃ Notched	KJ/m2	2
Izod Impact Strength	180/1A	-30 ℃ Notched	KJ/m2	-
Charpy Impact Strength	179	23 ℃ Notched	KJ/m2	2
Charpy Impact Strength	179	-30 ℃ Notched	KJ/m2	-
Vicat Softening Temp.	306	1 Kg,50 ℃/hr	℃	115
Vicat Softening Temp.	306	5 Kg,50 ℃/hr	℃	107
Heat Distortion Temp.	75/A	1.8 MPa Unannealed	℃	95
Heat Distortion Temp.	75/A	1.8 MPa Annealed	℃	104
Coefficient of Linear Thermal Expansion	11359	-	-	6 X 10-5
Flammability	-	UL-94	-	1.5mm HB
Mold Shrinkage	294-4	-	%	0.2~0.6
Symbol	1043	-	-	>PMMA<